Coater having substrate cleaning device and coating deposition methods employing such coater

ABSTRACT

A coater having a substrate cleaning device is disclosed. Also disclosed are methods of processing substrates in a coater equipped with a substrate cleaning device. The substrate cleaning device comprises an ion gun (i.e., an ion source) that is positioned beneath a path of substrate travel (e.g., beneath a substrate support) extending through the coater and that is adapted for treating a bottom major surface of a substrate. Certain embodiments involve an upward coating apparatus that is further along the path of substrate travel than the substrate cleaning device. In some embodiments of this nature, the upward coating apparatus is configured for depositing a photocatalytic coating upwardly onto the bottom major surface of the substrate. Certain embodiments of the invention involve a downward coating apparatus, wherein the substrate cleaning device is further along the path of substrate travel than the downward coating apparatus. Some embodiments of this nature also involve an upward coating apparatus that is further along the path of substrate travel than the substrate cleaning device.

This application claims the benefit of U.S. Provisional Application No.60/437,518, filed 31 Dec. 2002.

FIELD OF THE INVENTION

The present invention provides a coater in which coatings are applied tosubstrates. Also provided are methods of depositing coatings onsubstrates. More specifically, the invention provides a coater andmethods in which thin films are applied to glass sheets or othersheet-like substrates.

BACKGROUND OF THE INVENTION

The bottom surface of a sheet-like substrate (e.g., a glass sheet) canbe contaminated in situ (i.e., while the substrate is inside a coater)due to overspray from a downward coating operation. For example, whenmaterial is sputtered downwardly onto the top surface of a substrate,some of the sputtered material can actually find its way onto thesubstrate's bottom surface. This overspray phenomenon has been found toleave unwanted coating on marginal portions of the substrate's bottomsurface. This can create an undesirable “picture frame” effect on thesubstrate. Thus, when a downward coating operation is performed on asubstrate, it would be desirable to provide means for cleaning (e.g.,removing any unwanted oversprayed coating from) the substrate's bottomsurface after the downward coating operation is performed. It would beparticularly desirable to provide in situ means (i.e., means inside acoater) for cleaning the bottom surface of a substrate after its topsurface has been coated by a downward coating operation.

Further, when a desired coating is applied to the bottom surface of asubstrate by an upward coating operation after the top surface of thesubstrate has been coated by a downward coating operation, the marginalportions of the bottom surface can end up carrying both the desiredcoating and unwanted overspray from the downward coating operation,while the central portion of this surface carries only the desiredcoating. The resulting non-uniformity/picture frame effect, even if notdiscernable with the naked eye, is undesirable in that it can throw thecoated substrate outside desired specifications. Thus, when a downwardcoating operation is performed prior to an upward coating operation, itwould be particularly desirable to provide means for cleaning the bottomsurface after the downward coating operation but before the upwardcoating operation.

Applying coating in an upward direction onto the bottom surface of asubstrate can be highly advantageous. Upward coating operations can beadvantageously performed in a coater in addition, or as an alternative,to downward coating operations. Particularly advantageous upwardsputtering methods and equipment are described in U.S. patentapplication Ser. Nos. 09/868,542, 09/868,543, 09/979,314, 09/572,766,and 09/599,301, the entire contents of each of which are incorporatedherein by reference. In conjunction with upward coating technology, itwould be desirable to provide means for cleaning the bottom surface of asubstrate before (preferably shortly before) such surface is coated byan upward coating operation. It would be particularly desirable toprovide in situ means for cleaning the bottom surface of a substratebefore such surface is coated by an upward coating operation.

When a substrate is transported through a coater using a substratesupport, the substrate can be left with traces of contact from thesupport. Substrates are commonly conveyed through coaters usingspaced-apart transport rollers, such that the bottom surface of eachsubstrate is in direct contact with the rollers during conveyance. Therollers can leave traces of contact on the bottom surface of eachsubstrate. While these traces of contact tend to be relatively minor(and completely acceptable for many applications), it would be desirableto provide means for assuring that any such traces of contact arecompletely removed from the bottom surface of the substrate before suchsurface is coated by an upward coating operation.

It would be particularly desirable to perform an ion beam treatment onthe bottom surface of a substrate before applying a photocatalyticcoating to such surface by an upward coating operation. This is done incertain embodiments of the present invention, for example, to facilitatedepositing a high quality photocatalytic coating. This method isparticularly preferred in embodiments wherein it is desired to deposit aparticularly thin high quality photocatalytic coating.

SUMMARY OF THE INVENTION

In certain embodiments, the invention provides a coater adapted forapplying coating onto a sheet-like substrate. The coater comprises asubstrate support defining a path of substrate travel extending throughthe coater. The coater also comprises an ion gun positioned beneath thepath of substrate travel and adapted for cleaning a bottom major surfaceof the substrate. In some embodiments, the coater further includes anupward coating apparatus positioned beneath the path of substrate travelat a location further along the path of substrate travel than the iongun. In one particular embodiment of this nature, the upward coatingapparatus is an upward sputtering apparatus that includes a lowersputtering target comprising a titanium-containing target material.

In certain embodiments, the invention provides a method of processing asheet-like substrate. The method comprises providing a coater adaptedfor applying coating onto the substrate. The coater comprises asubstrate support defining a path of substrate travel extending throughthe coater. The coater also comprises an ion gun positioned beneath thepath of substrate travel. The substrate is conveyed along the path ofsubstrate travel and the ion gun is operated to emit ions (e.g.,upwardly) toward a bottom major surface of the substrate. The ionspreferably comprise accelerated ions that form an ion beam (e.g., afocused ion beam) and strike the bottom major surface of the substrate,thereby treating (e.g., cleaning) the substrate's bottom major surface.In some embodiments, the coater further includes an upward coatingapparatus positioned beneath the path of substrate travel at a locationfurther along the path of substrate travel than the ion gun. In oneparticular embodiment of this nature, the upward coating apparatus isoperated to apply a photocatalytic coating on the previously ion-treatedbottom major surface of the substrate.

Certain embodiments of the invention provide a method of processing asheet-like substrate. In these embodiments, the method comprisesproviding a coater that is adapted for applying coating onto thesubstrate. The coater comprises a substrate support defining a path ofsubstrate travel extending through the coater. A downward coatingapparatus is positioned in the coater above the path of substratetravel. An ion gun is positioned beneath the path of substrate travel.In the present embodiments, the ion gun is at a location further alongthe path of substrate travel than the downward coating apparatus(preferably, this ion gun is not vertically aligned with any downwardcoating apparatus). The method comprises conveying the substrate alongthe path of substrate travel, operating the downward coating apparatusto coat a top major surface of the substrate, and thereafter operatingthe ion gun to emit an ion beam toward a bottom major surface of thesubstrate. Here, the operation of the ion gun is performed to remove,substantially if not entirely, from the bottom major surface of thesubstrate any oversprayed coating that was inadvertently deposited uponmarginal portions of the bottom major surface of the substrate duringthe operation of the downward coating apparatus (in some cases, alsoshaving off some of the substrate material). In the present embodiments,the coater need not have any upward coating apparatus.

Certain embodiments of the invention provide a coater adapted forapplying coating onto a sheet-like substrate. In these embodiments, thecoater comprises a substrate support defining a path of substrate travelextending through the coater. A downward coating apparatus is positionedabove the path of substrate travel and is adapted for coating a topmajor surface of the substrate. An ion gun is positioned beneath thepath of substrate travel and is adapted for cleaning a bottom majorsurface of the substrate. In the present embodiments, the ion gun is ata location further along the path of substrate travel than the downwardcoating apparatus such that the ion gun is adapted to remove,substantially if not entirely, from the bottom major surface of thesubstrate oversprayed coating inadvertently deposited upon marginalportions of the bottom major surface of the substrate during operationof the downward coating apparatus. In the present embodiments, thecoater need not have any upward coating apparatus.

In certain embodiments, the invention provides a method of processing asheet-like substrate. In these embodiments, the method comprisesproviding a coater adapted for applying coating onto the substrate. Thecoater comprises a substrate support defining a path of substrate travelextending through the coater. An ion gun is positioned beneath the pathof substrate travel. In the present embodiments, an upward coatingapparatus is positioned beneath the path of substrate travel at alocation further along the path of substrate travel than the ion gun.The method comprises conveying the substrate along the path of substratetravel, operating the ion gun to emit ions (e.g., an ion beam) toward abottom major surface of the substrate (preferably such ions form an ionbeam comprising accelerated ions that strike the bottom major surface ofthe substrate), and operating the upward coating apparatus to deposit aphotocatalytic coating on the bottom major surface of the substrate. Inthe present embodiments, the coater need not have any downward coatingapparatus.

Certain embodiments of the invention provide a coater adapted forapplying coating onto a sheet-like substrate. The coater comprises asubstrate support defining a path of substrate travel extending throughthe coater. An ion gun is positioned beneath the path of substratetravel. In these embodiments, an upward coating apparatus is positionedbeneath the path of substrate travel at a location further along thepath of substrate travel than the ion gun. In the present embodiments,the upward coating apparatus preferably comprises a titanium-containingsource material (e.g., a lower sputtering target comprising atitanium-containing target material). In the present embodiments, thecoater need not have any downward coating apparatus.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 illustrates a coater having disposed therein an ion gun inaccordance with certain embodiments of the present invention;

FIG. 2 illustrates a coater having disposed therein an ion gun and anupward coating apparatus in accordance with certain embodiments of theinvention;

FIG. 3 illustrates a coater having disposed therein a downward coatingapparatus, an ion gun, and an upward coating apparatus in accordancewith certain embodiments of the invention;

FIG. 4 illustrates another coater having disposed therein a downwardcoating apparatus, an ion gun, and an upward coating apparatus inaccordance with certain embodiments of the invention;

FIG. 5 illustrates a further coater having disposed therein a downwardcoating apparatus, an ion gun, and an upward coating apparatus inaccordance with certain embodiments of the invention; and

FIG. 6 illustrates a coater having disposed therein a downward coatingapparatus and an ion gun in accordance with certain embodiments of theinvention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The following detailed description is to be read with reference to thedrawings, in which like elements in different drawings have likereference numerals. The drawings, which are not necessarily to scale,depict selected embodiments and are not intended to limit the scope ofthe invention. Skilled artisans will recognize that the examplesprovided herein have many useful alternatives that fall within the scopeof the invention.

The present invention involves a coater 5 adapted for applying coatingonto a sheet-like substrate 30. As shown in FIG. 1, the coater 5includes at least one chamber 10 in which a controlled environment canbe established. Preferably, the chamber is adapted for use in lowpressure deposition processes (e.g., in vacuum deposition processes).For example, the chamber 10 preferably is adapted for use at (e.g., isadapted for establishing and maintaining therein) a total gas pressureof less than about 140 torr., more preferably less than about 0.1 torr.,and perhaps most commonly between about 1 mtorr. and about 0.1 torr.(e.g., between about 1 mtorr. and about 30 mtorr.). Thus, in certainembodiments, the chamber 10 is adapted for use at (e.g., is providedwith conventional gas delivery and pumping systems adapted forestablishing and maintaining) pressures within any range or rangesdescribed in this paragraph.

The coater comprises one or more chambers. It will be apparent toskilled artisans that any desired number of chambers can be used. Insome cases, the coater comprises a series of connected chambers. Forexample, the coater may comprise a sputtering line. Sputtering lines arewell known in the present art. Briefly, a sputtering line comprises aseries of sputtering chambers aligned and connected such that sheet-likesubstrates (e.g., a plurality of spaced-apart substrates, such as glasssheets) supported horizontally on spaced-apart transport rollers can beconveyed sequentially through the chambers of the sputtering line.Typically, the sputtering line includes narrow evacuated tunnels, whichconnect adjacent chambers, through which the horizontally-orientedsubstrates are conveyed from one chamber to the next. Thus, substratesare typically conveyed sequentially through all of the chambers of asputtering line during sputtering. It will be appreciated that thepresent coater 5 may include a plurality of chambers aligned andconnected in this manner, regardless of the particular depositionprocesses that are performed in such chambers.

The present coater 5 can include chambers adapted for carrying outdifferent deposition processes. For example, the coater can include oneor more chambers in which sputtering is performed and one or morechambers in which evaporation is performed. Further, the coater caninclude one or more chambers in which sputtering is performed and one ormore chambers in which chemical vapor deposition is performed.Similarly, the coater can include one or more chambers in whichsputtering is performed and one or more chambers in which ion beamcoating deposition is performed. Still further, the coater can includeone or more chambers in which chemical vapor deposition is performed andone or more chambers in which evaporation is performed. Variousalternatives of this nature will be apparent to skilled artisans giventhe present teaching as a guide.

A variety of substrates are suitable for use in the present invention.In most cases, the substrate is a sheet of transparent material (i.e., atransparent sheet). However, the substrate is not required to betransparent. For example, opaque substrates may be useful in some cases.However, it is anticipated that for most applications, the substratewill comprise a transparent or translucent material, such as glass orclear plastic. In many cases, the substrate will be a glass sheet. Avariety of known glass types can be used, and soda-lime glass isexpected to be preferred.

Substrates of various size can be used in the present invention. Anadvantage of the coater 5 is that it can be used to process large-areasubstrates. Certain embodiments involve a substrate having a width of atleast about 0.5 meter, preferably at least about 1 meter, perhaps morepreferably at least about 1.5 meters (e.g., between about 2 meters andabout 4 meters), and in some cases at least about 3 meters.

Substrates of various thickness can be used in the present invention.Commonly, substrates with a thickness of about 1-5 mm are used. Someembodiments involve a substrate with a thickness of between about 2.3 mmand about 4.8 mm, and perhaps more preferably between about 2.5 mm andabout 4.8 mm. In some cases, a sheet of glass (e.g., soda-lime glass)with a thickness of about 3 mm is used.

The coater 5 comprises a substrate support 40 defining a path ofsubstrate travel 60 extending through the coater. Preferably, the pathof substrate travel extends substantially horizontally through thecoater. In the embodiments of FIGS. 1-3, the substrate support 40defines a path of substrate travel 60 extending through the coater 5between a chamber inlet 15 and a chamber outlet 20. In embodimentswherein the coater 5 comprises more than one chamber, the chambers aretypically connected such that the path of substrate travel 60 extendsthrough each of the chambers between a coater inlet and a coater outlet.

Preferably, the substrate support 40 is configured for maintaining(e.g., supporting) the substrate in a horizontal configuration while thesubstrate is being coated (e.g., during conveyance of the substratethrough the coater). Thus, the support 40 desirably is adapted to conveya sheet-like substrate 30, and preferably multiple sheet-like substratesthat are spaced-apart from one another, through the coater whilemaintaining the/each substrate 30 in a horizontal orientation (e.g.,wherein a top major surface 14 of the/each substrate 30 is upwardlyoriented while a bottom major surface 12 of the/each substrate 30 isdownwardly oriented). In the embodiments shown in the present figures,the substrate support 40 comprises a plurality of spaced-apart transportrollers 310. Typically, at least one of the rollers is rotated (e.g., byenergizing a motor operably connected to the roller) such that thesubstrate 30 is conveyed through the chamber 10 along the path ofsubstrate travel 60. When the substrate is conveyed over such rollers,the bottom surface 12 of the substrate 30 is in direct physical (i.e.,supportive) contact with the rollers. The substrate is typicallyconveyed through the coater at a speed of about 100-500 inches perminute. In FIGS. 3-6, embodiments are illustrated wherein the substrateis a sheet of glass that is on the substrate support during conveyance,and wherein other sheets of glass are also on the substrate support,such sheets of glass being spaced-apart from one another on thesubstrate support and conveyed in such a spaced-apart configuration.While the illustrated substrate support 40 comprises a plurality ofspaced-apart rollers 310, it is to be appreciated that other types ofsubstrate supports can be used.

In embodiments wherein the substrate support 40 is formed by transportrollers, the rollers can be of any conventional structure. It has beenfound that good results can be obtained by employing cylindrical (e.g.,aluminum) rollers about which a rope is spirally wound, with such ropeproviding the surface with which the substrate is in direct contact. Therope can be formed of Kevlar™, i.e., poly-para-phenyleneterephthalamide, or another polymer (e.g., nylon-like polymer).Preferably, a high melting point polymer is used (e.g., a polymer havinga melting point above the maximum processing temperature established ina desired deposition process, e.g., at least about 165 degrees C., morepreferably at least about 200 degrees C., and perhaps optimally at leastabout 400 degrees C.). Rollers carrying a spirally-wound rope (or aplurality of individual bands) are particularly desirable forembodiments wherein an upward coating process is performed, as the ropereduces the area of contact between the rollers and the substrate andthus provides a particularly non-damaging support for the substrate'sfreshly-coated bottom surface. Thus, in certain embodiments, thesubstrate support 60 comprises a plurality of spaced-apart rollers eachhaving at least one rope disposed about the roller.

In the embodiment of FIG. 1, an ion gun 50 is positioned beneath (i.e.,at a lower elevation than) the path of substrate travel 60. The ion gunpreferably is disposed within (i.e., inside) the coater 5. For example,the ion gun 50 can be disposed within a chamber 10 of the coater 5 thatis adapted for use at a total gas pressure of less than about 140 torr.,more preferably less than about 0.1 torr., and perhaps most commonlybetween about 1 mtorr. and about 0.1 torr. (e.g., between about 1 mtorr.and about 30 mtorr.). The ion gun 50 can be mounted within such achamber 10 by any conventional means (e.g., using any conventionmounting hardware). For example, the ion gun can be secured to a flangeor flanges extending from a floor and/or sidewall of the coater.

The mounted ion gun preferably is adapted for treating (e.g., foraccelerating ions at) the bottom surface of the substrate 30 as it isconveyed along the path of substrate travel 60. Thus, the mounted iongun preferably is positioned beneath the path of substrate travel 60,such that when the ion gun 50 is operated it emits (e.g., upwardlybetween two spaced-apart transport rollers) ions, preferably a beam ofions, toward the bottom major surface 12 of the substrate 30. It will beappreciated that the ion gun 50 will typically be operated when thesubstrate 30 is on the support 40 at a portion of the path of substratetravel 60 adjacent (e.g., directly above) the ion gun.

The ion gun 50 desirably is adapted for emitting ions that span (e.g.,an ion beam that spans) substantially the entire width (preferably theentire width) of the substrate 30. For example, the ion gun preferablyemits a curtain-like ion beam that spans the entire width of thesubstrate's bottom major surface 12. Thus, the ion gun 50 preferably isadapted for treating (e.g., cleaning) the entire bottom surface 12 ofthe substrate 30. This can be accomplished in several ways. One way isby providing a single ion gun (which may have one ion source or multipleion sources) that is capable of generating an ion beam or beams spanningsubstantially the entire width (preferably the entire width) of thesubstrate. Another way is to provide a plurality of ion guns, whichtogether generate a collective ion beam or beams spanning substantiallythe entire width of the substrate. For example, two or more ion guns canbe configured and operated such that their combined beams span theentire width of the substrate.

The invention is particularly advantageous in processing large areasubstrates, such as glass sheets for architectural and automotive glassapplications. Substrates of this nature commonly have a width of atleast about .5 meter, more commonly at least about one meter, andtypically greater than about 1.5 meters (e.g., between about 2 metersand about 4 meters). Accordingly, the ion gun 50 is preferably adaptedto emit an ion beam that spans the entire width of such a substrate(i.e., a substrate having a width in one or more of these ranges). Withlarge area substrates in particular (especially those formed of glass),it is desirable to convey the substrates through the coater in ahorizontal orientation, rather than in a vertical orientation.

The ion gun 50 can be any ion source. In certain preferred embodiments,the ion gun is adapted to ionize gas molecules and then focus,accelerate, and emit them as a narrow beam (i.e., as an ion beam). Forexample, the ion gun can be a linear ion source. The ion gun, however,is by no means required to emit ions in the form of a beam. Some ionguns are not operable in low pressure environments (e.g., under vacuumconditions). The present ion gun 50, however, preferably is operable inlow pressure environments (e.g., in a vacuum deposition chamber). Forexample, the ion gun 50 is preferably adapted to operate in environmentshaving a total gas pressure of less than about 140 torr., morepreferably less than about 0.1 torr., and perhaps most commonly betweenabout 1 mtorr. and about 0.1 torr. (e.g., between about 1 mtorr. andabout 30 mtorr.).

The present ion gun is preferably one that accelerates ionselectrodynamically, rather than electrostatically. The use ofelectrostatic fields to transfer, collect, or manipulate ions is wellknown. Typically, electrostatic fields are used with ion guns thatoperate at or near atmospheric pressure. Electrostatic fields tend to beless desirable for ion guns that operate in low pressure environments(e.g., under vacuum). To the contrary, electrodynamic fields are moreeffective for accelerating ions in low pressure environments. In certainpreferred embodiments, therefore, the ion gun comprises an ion sourcethat accelerates ions electrodynamically.

In certain particularly preferred embodiments, the ion gun 50 is ananode layer ion source. Anode layer ion sources accelerate ionselectrodynamically, rather than electrostatically. As a result, they aredesirable for use in low pressure environments. Further, anode layer ionsources are compatible with a wide variety of working gases, includingargon, oxygen, nitrogen, hydrocarbons, and mixtures of such gases.Suitable ion sources of this nature are commercially available fromVeeco (Ft. Collins, Colo., USA) under the trade names ALS 106C, ALS144L, ALS 340L, ALS 340W. Reference is made to U.S. Pat. No. 6,147,354(Maishev et al.), the entire contents of which are incorporated hereinby reference, in which there is described operation of an anode-layertype ion source in a vacuum chamber.

With continued reference to FIG. 1, it can be appreciated that the iongun 50 is disposed within the coater 5. As noted above, the ion gun 50may be provided (e.g., mounted) in a chamber 10 of the coater 5 that isadapted for use at a total gas pressure of less than about 140 torr.,more preferably less than about 0.1 torr., and perhaps most commonlybetween about 1 mtorr. and about 0.1 torr. (e.g., between about 1 mtorr.and about 30 mtorr.).

In embodiments wherein the substrate support 40 is provided in the formof spaced-apart transport rollers 310, the spacing of the rollers 310 ispreferably kept fairly small to permit small substrates to be processedwithout any significant risk of having the substrates fall between thespaced-apart rollers. The maximum safe spacing is preferably determinedon a case-by-case basis for a desired range of substrate sizes.

The ion gun 50 and the rollers 310 preferably are configured such thatthe ion gun 50 is adapted to emit an ion beam upwardly between anadjacent pair of the rollers (this pair of rollers preferably isgenerally above the ion gun). It can be appreciated that there is a gap45 between these two rollers. If so desired, this pair of rollers can bespaced further apart than other rollers in the coater 5, such that thisparticular gap 45 is wider than other such gaps in the coater. This maybe done to minimize any interference of the rollers with the ion beam.

Thus, in certain embodiments the ion gun 50 is positioned beneath aportion of the path of substrate travel 60 where an adjacent pair ofrollers are mounted further apart than other adjacent rollers in thecoater. In such embodiments, there is a gap 45 between the two rollersgenerally above/over the ion gun 50 that is wider than the gaps betweenother adjacent roller pairs in the coater 5. In such embodiments, therollers in other areas of the chamber 10 can have conventional spacing.

It may also be desirable if certain rollers in the chamber 10 areremovable, such that the chamber 10 can be readily converted between afirst configuration, wherein a particularly wide gap 45 is providedbetween the two transport rollers nearest the ion gun, and a secondconfiguration having a conventional roller arrangement wherein all ofthe rollers are evenly spaced.

Instead of mounting the rollers above the ion gun 50 further apart,these rollers could instead be made smaller in diameter. Conventionaltransport rollers are hollow metal tubes. If so desired, particularlysmall diameter tubes could be used. In such cases, it may be desirableto stiffen the rollers, e.g., by filling them with rigid foam. In orderto maintain the same transport speed of a substrate along the support60, these small-diameter rollers could be rotated more rapidly, e.g., bymeans of a pair of gears having an appropriate gear ratio. In oneembodiment, the two rollers between which the ion gun 50 emits ions aresmaller (i.e., have a smaller diameter) than other rollers in thecoater. While the foregoing embodiments are expected to be advantageous,it is to be understood that the ion gun 50 can simply be aligned beneatha gap that results from conventional roller spacing.

As can be appreciated with reference to FIGS. 2-5, the coater 5 incertain embodiments includes an upward coating apparatus 55. Whenprovided, the upward coating apparatus 55 is adapted for coating thebottom major surface 12 of the substrate 30. In embodiments of thisnature, the ion gun 50 and the upward coating apparatus 55 arepreferably both disposed (e.g., mounted) within the coater 5. If sodesired, the ion gun 50 and an upward coating apparatus 55 can both bedisposed in a common chamber (i.e., in the same chamber) of the coater5. This, however, is by no means required. The ion gun 50 and the upwardcoating apparatus 55, when it 55 is provided, are preferably bothpositioned beneath (i.e., at a lower elevation than) the path ofsubstrate travel 60.

In certain particularly advantageous embodiments, an upward coatingapparatus 55 is positioned (e.g., mounted) at a location further alongthe path of the substrate travel 60 than the ion gun 50. By positioningan upward coating apparatus 55 at a location further along the path ofsubstrate travel 60 than the ion gun 50, the ion gun is adapted fortreating (e.g., cleaning) the bottom major surface 12 of the substrate30 before the upward coating apparatus is operated to coat the bottommajor surface of the substrate.

When provided, the upward coating apparatus 55 is preferably positionedbeneath a gap 145 between an adjacent pair of transport rollers 310.This gap 145 may result from conventional roller spacing. Alternatively,this gap 145 may be wider than the gaps between other adjacent rollerpairs in the coater 5. This can be accomplished in the manner describedabove with reference to the transport rollers over the ion gun (i.e., bymounting the rollers that define this gap 145 further apart and/or bydecreasing the size of these rollers).

When provided, the upward coating apparatus 55 can be any type of upwardcoating apparatus. For example, this upward coating apparatus 55 can bea sputter coating apparatus, an ion beam coating deposition apparatus,an evaporation coating apparatus, a chemical vapor deposition apparatus,or any other apparatus that is adapted for performing an upward coatingoperation.

In certain preferred embodiments, the optional upward coating apparatus55 is an upward sputtering apparatus. For example, this apparatus 55 mayinclude a lower sputtering target 360, 360 a, 360 b positioned beneaththe path of substrate travel. This upward coating apparatus may includea lower gas distribution system (e.g., comprising at least onegas-delivery outlet) adapted for delivering sputtering gas to the lowerregion of the coater (i.e., the region of the coater below the path ofsubstrate travel). This is perhaps best appreciated with reference toFIGS. 4 and 5, wherein the illustrated coaters include lower sputteringtargets 360 a, 360 b and lower gas distribution pipes 375 adjacent thelower targets. Also shown in FIGS. 4 and 5 are optional lower anodes370, which preferably are below the path of substrate travel. Whenprovided, the lower anodes 370 are typically positioned adjacent thelower targets 360, 360 a, 360 b. Upward sputtering systems are describedin U.S. patent application Ser. Nos. 09/868,542, 09/868,543, 09/979,314,09/572,766, and 09/599,301.

In other embodiments, the optional upward coating apparatus 55 is anevaporation coating apparatus. An apparatus 55 of this nature typicallycomprises a source of coating material to be evaporated. This sourcematerial will typically be positioned beneath the path of substratetravel 60. The source material can be provided in the form of a boat,crucible, strip, or coil that contains, or is formed of, the desiredsource material. Means are also typically provided for delivering energyto such source material. For example, the source material may beprovided in conjunction with a heat source adapted for heating suchmaterial by direct or indirect resistance, by thermal conduction, byradiation or induction, by electron beam, or by laser irradiation orarcing.

Various processes for coating substrates by evaporation are known in theart. Briefly, evaporation is a form of physical vapor deposition thatinvolves delivering energy to a source material in vacuum until itevaporates at adequate rates. The source material is transported inresidual gas phase to the substrate, where such gas phase materialcondenses upon the substrate and forms the desired coating. When theoptional upward coating apparatus 55 is an evaporation apparatus, it maybe desirable to maintain the chamber at pressures on the order ofbetween about 10⁻⁶ mbar. and about 10⁻⁴ mbar.

In other embodiments, the optional upward coating apparatus 55 is achemical vapor deposition (i.e., CVD) apparatus. An apparatus of thisnature typically comprises a gas outlet for delivering precursor gas tothe lower region of the coater. Preferably, this gas outlet ispositioned below the path of the substrate travel 60, such that from theprecursor gas, coating material condenses upon the bottom surface of thesubstrate 30. A CVD apparatus of this nature will typically comprise agas supply from which the precursor gas is delivered through the gasoutlet and into the lower region of the coater. Any known CVD apparatuscan be used. If so desired, this upward coating apparatus can be aplasma-enhanced chemical vapor deposition apparatus of the typedescribed in U.S. patent application Ser. No. 10/373,703, entitled“Plasma-Enhanced Film Deposition” (Hartig), filed on Dec. 18, 2002.

In certain embodiments, the upward coating apparatus 55 comprises an iongun. This ion gun can be part of any known ion-assisted deposition(i.e., IAD) process. For example, this ion gun can be part of an ionbeam sputter deposition source comprising a sputtering target againstwhich this ion gun accelerates ions, such that atoms of the targetmaterial are ejected from the target upwardly toward the substrate.Alternatively, this ion gun can be part of an ion-assisted evaporationapparatus, such as those disclosed in the publication “Ion-Based MethodsFor Optical Thin Film Deposition” (Journal of Material Science; J. P.Marting, 21 (1986) 1-25), the entire teachings of which are incorporatedherein by reference. These types of IAD methods are known in the art, asare various other suitable IAD methods.

In certain embodiments, the coater 5 comprises a downward coatingapparatus 65 that is adapted for coating a top major surface 14 of thesubstrate 30. Embodiments of this nature are exemplified in FIGS. 3-6.In such embodiments, the ion gun 50 is preferably positioned (e.g.,mounted) at a location further along the path of substrate travel 60than the downward coating apparatus 65. The ion gun 50 is thus adaptedfor removing, substantially if not entirely, from the bottom majorsurface of the substrate oversprayed coating that has been inadvertentlydeposited upon marginal portions of the bottom major surface of thesubstrate during operation of the downward coating apparatus. In thepresent embodiments (which involve a downward coating apparatus,together with an ion gun positioned below the path of substrate travelat a location further along the path of substrate travel than thedownward coating apparatus), no upward coating apparatus is required inthe coater. However, in FIGS. 3-5, an optional upward coating apparatus55 is positioned at a location further along the path of substratetravel 60 than the ion gun 50. Thus, any oversprayed coating on thebottom surface 12 of the substrate 30 can be substantially, if notentirely, removed before this surface 12 is coated during operation ofthe optional upward coating apparatus 55.

When provided, the downward coating apparatus 65 can be any type ofdownward coating apparatus. In certain preferred embodiments, thedownward coating apparatus 65 is a downward sputtering apparatus. Insuch embodiments, the downward sputtering apparatus comprises an uppersputtering target 320, 320 c, 320 d, 320 e, 320 f positioned above thepath of substrate travel 60. Conjointly, the coater can be provided withupper gas distribution pipes 335 (e.g., having outlets that are)positioned above the path of substrate travel 60. It will typically bepreferred to also provide upper anodes 330 above the path of substratetravel 60. When provided, the upper anodes 330 are preferably positionedadjacent upper targets. As noted above, each target in FIGS. 2-6 isdepicted as being a cylindrical target, although planar targets can beused as well.

In other embodiments, the optional downward coating apparatus 65comprises a chemical vapor deposition apparatus. Such an apparatus maycomprises a gas delivery outlet for delivering precursor gas to theupper region of the coater (i.e., the region of the coater above thepath of substrate travel). Preferably, this gas outlet is positionedabove the path of substrate travel 60, such that from the precursor gas,coating material condenses upon the top major surface 14 of thesubstrate 30. A CVD apparatus of this nature will typically comprise agas supply from which the precursor gas is delivered through the gasoutlet and into the upper region of the coater. If so desired, thisdownward coating apparatus can be a plasma-enhanced chemical vapordeposition apparatus of the type described in U.S. patent applicationSer. No. 10/373,703, entitled “Plasma-Enhanced Film Deposition”(Hartig), filed on Dec. 18, 2002.

In certain embodiments, the downward coating apparatus comprises anupper ion gun. This upper ion gun can be part of any desired downwardion-assisted deposition process. For example, this upper ion gun can bepart of an ion beam sputter deposition source comprising a sputteringtarget against which this ion gun accelerates ions, such that atoms ofthe target material are ejected from the target downwardly toward thesubstrate. This type of IAD method is known in the art, as are variousother suitable IAD methods.

It has been discovered that the bottom surface of a substrate can becoated inadvertently due to overspray from a downward coating operation.For example, when material is sputtered downwardly onto the top surfaceof a substrate, some of the sputtered material can actually find its wayonto the bottom surface of the substrate. This phenomenon has been foundto leave unwanted coating on marginal portions of the substrate's bottomsurface. This can create an undesirable picture frame effect on thesubstrate. Further, if a desired coating is subsequently applied to thebottom surface by an upward coating operation, the marginal portions ofthis surface will end up carrying both the desired coating and theunwanted oversprayed coating, while the central portion of this surfacecarries only the desired coating. This non-uniformity/picture frameeffect can have a variety of adverse effects on the intended coatingproperties/the desired specifications.

These particular overspray problems can be eliminated by positioning theion gun 50 further along the path of substrate travel 60 (preferably ata location beyond where the substrate is exposed to film deposition fromthe downward coating apparatus) than the downward coating apparatus 65.This enables the ion gun 50 to remove from the bottom surface 12 of thesubstrate 30 oversprayed coating (in some cases, the ion gun is operatedso it also mills away a small thickness of glass from the bottom surfaceof a glass substrate) that has been inadvertently deposited on marginalportions of the substrate's bottom surface 12 during operation of thedownward coating apparatus 65. This also tends to substantially reduce,if not eliminate, any traces of contact on the substrate's bottomsurface that may have resulted from conveying the substrate through thecoater on the substrate support. If an upward coating apparatus 55 isalso provided, it is preferably located further along the path ofsubstrate travel 60 than the ion gun 50. This enables the ion gun 50 toremove (substantially if not entirely) from the bottom surface 12 of thesubstrate 30 oversprayed coating that has been inadvertently depositedon marginal portions of the substrate's bottom surface 12 duringoperation of the downward coating apparatus 65 before this surface 12 iscoated during operation of the upward coating apparatus 55.

It has also been discovered that a further overspray problem can resultwhen coating is applied upwardly onto the bottom surface 12 of asubstrate 30 before coating is applied downwardly onto the top surface14 of the substrate 30. In particular, the desired coating properties onthe substrate's bottom surface 12 can be compromised when material fromthe downward coating operation oversprays the coating that haspreviously been applied upwardly onto the substrate's bottom surface 12.Even if such oversprayed material has no apparent (e.g., readily visibleto the naked eye) effect on the coated substrate, it can compromise thedesired properties of the coated substrate. This can be particularlyproblematic when the substrate's bottom surface is intended to haveparticular surface properties (e.g., when the substrate's bottom surfaceis intended to carry a surface-effect coating), such as photoactivity,hydrophilicity, hydrophobicity, or the like. The oversprayed coating onthe substrate's bottom surface may nullify or reduce such intendedsurface properties.

To obviate this problem, the upward coating apparatus 55 can optionallybe disposed in a final chamber (in some cases, in the final depositionzone of the final chamber) of the coater. This final chamber may be thelast chamber along the path of substrate travel 60. Alternatively, thisfinal chamber may be the last operating chamber (i.e., the last chamberin which any film deposition operation is performed) along the path ofsubstrate travel. In such cases, the coater may include one or morenon-operated chambers further along the path of substrate travel. Theinventors have discovered these embodiments to be advantageous in thatonce this upward coating apparatus is operated to apply a desiredcoating on the bottom major surface of the substrate, this desiredcoating will not be subjected to any subsequent overspray, such as mayotherwise occur if the thus-coated substrate were subsequently conveyedinto an active (i.e., operated) downward coating zone. Thus, in certainembodiments, operation of the upward coating apparatus is performedafter all other coating of the substrate in the coater has beenperformed. Similarly, in certain embodiments, the substrate is notconveyed beneath any operating/operated downward coating apparatus inthe coater after the operation of the upward coating apparatus, suchthat marginal portions of coating applied to the bottom major surface ofthe substrate will not be concealed by oversprayed coating from anysubsequent downward coating apparatus in the coater.

In certain embodiments wherein an upward coating apparatus is provided,the coater 5 is operated so as to deposit upon the bottom major surfaceof the substrate a coating (which in some cases comprises at least somehigh index film having a refractive index of at least about 2.3) havinga total optical thickness of less than about 690Å. In these embodiments,any traces of contact left on this coating from the substrate supportwill tend to be invisible or at least very difficult to perceive. Insome embodiments of this nature, the coater 5 is operated such that thetop major surface of the substrate is also coated with a coating,preferably with one having a total optical thickness of at least about1,000Å. In certain embodiments of this nature, wherein the coater has atleast one upward coating apparatus and a plurality of downward coatingapparatuses, the coater is operated to deposit a low-emissivity coatingon the top major surface of the substrate and to deposit asurface-effect coating on the bottom major surface of the substrate.Here, the surface-effect coating is preferably selected from the groupconsisting of a photocatalytic coating, a hydrophilic coating, and ahydrophobic coating. In some embodiments of this nature, thesurface-effect coating comprises titanium oxide and/or silicon oxide. Inone such embodiment, the surface-effect coating is a photocatalyticcoating comprising titanium oxide.

Low-emissivity coatings are well known in the art and typically includeat least one region of infrared-reflective film sandwiched between atleast two regions of transparent dielectric film. Theinfrared-reflective film, which typically comprises a conductive metalsuch as silver, gold, or copper, reduces the transmission of radiantheat through the coating. The transparent dielectric film is usedprimarily to reduce visible reflectance and to control other propertiesof the coatings, such as color. Commonly used transparent dielectricsinclude oxides of zinc, tin, indium, bismuth, and titanium, and alloysand mixtures thereof, as well as certain nitrides (e.g., siliconnitride). Useful low-emissivity coatings are described in U.S. patentapplication Ser. No. 09/728,435, the entire teachings of which areincorporated herein by reference.

Photocatalytic coatings typically comprise a semiconductor that canabsorb ultraviolet radiation and can photocatalytically degrade organicmaterials such as oil, plant matter, fats, and greases. The mostpowerful of the photocatalysts appears to be titanium oxide (e.g.,titanium dioxide). Useful photocatalytic coatings are described in U.S.Pat. No. 5,874,701 (Watanabe et al), U.S. Pat. No. 5,853,866 (Watanabeet al), U.S. Pat. No. 5,961,843 (Hayakawa et al.), U.S. Pat. No.6,139,803 (Watanabe et al), U.S. Pat. No. 6,191,062 (Hayakawa et al.),U.S. Pat. No. 5,939,194 (Hashimoto et al.), U.S. Pat. No. 6,013,372(Hayakawa et al.), U.S. Pat. No. 6,090,489 (Hayakawa et al.), U.S. Pat.No. 6,210,779 (Watanabe et al), U.S. Pat. No. 6,165,256 (Hayakawa etal.), and U.S. Pat. No. 5,616,532 (Heller et al.), the entire contentsof each of which are incorporated herein by reference.

Hydrophilic coatings have an affinity for water and tend to cause waterapplied to such coatings to sheet. Useful hydrophilic coatings aredescribed in U.S. patent applications Ser. Nos. 09/868,542, 09/868,543,09/599,301, and 09/572,766, the entire contents of each of which areincorporated herein by reference.

Hydrophobic coatings are applied to glass to repel water, thus causingwater on such coatings to bead up, rather than spreading into a sheet.Useful hydrophobic coatings are described in U.S. Pat. No. 5,424,130,issued to Nakanishi, et al., the entire teachings of which areincorporated herein by reference.

As noted above, the invention provides certain embodiments wherein thecoater includes an upward coating apparatus that is positioned beneaththe path of substrate travel at a location further along the path ofsubstrate travel than the ion gun. In some such embodiments, theinvention comprises operating the upward coating apparatus to coat thebottom major surface of the substrate after the ion gun has beenoperated to treat the bottom major surface of the substrate. In someembodiments of this nature, operation of the upward coating apparatuscomprises depositing on the bottom major surface of the substrate asurface-effect coating selected from the group consisting of aphotocatalytic coating, a hydrophilic coating, and a hydrophobiccoating. In these embodiments, the coater need not have any downwardcoating apparatus. In some cases, the surface-effect coating comprisestitanium oxide and/or silicon oxide. For example, the surface-effectcoating in one such case is a photocatalytic coating comprising titaniumoxide.

Thus, in certain embodiments, an upward coating apparatus 55 in thecoater 5 is adapted for depositing a high quality photocatalytic coatingonto the bottom surface 12 of the substrate 30 after ion bombarding thissurface 12 using a preceding ion gun 50. In these embodiments, theupward coating apparatus 55 that is adapted for depositing thephotocatalytic coating onto the bottom surface 12 of the substrate 30 islocated further along the path of substrate travel than the ion gun 50.In certain preferred embodiments, a particularly thin high qualityphotocatalytic coating is deposited on the bottom surface of thesubstrate using this upward coating apparatus after the bottom surfacehas been ion treated using the ion gun 50. In these embodiments, thethin high quality photocatalytic film preferably is deposited at a totaloptical thickness of less than about 690Å.

Thus, in certain embodiments, the optional upward coating apparatus 55is adapted for applying a photocatalytic coating. In some embodiments ofthis nature, the upward coating apparatus 55 is adapted for applying aphotocatalytic coating that comprises (perhaps more preferably consistsessentially of, and perhaps optimally consists of) titanium oxide. Inthese embodiments, the upward coating apparatus desirably comprises asource or sources of titanium and oxygen. For example, the upwardcoating apparatus 55 can optionally include a lower sputtering targetcomprising titanium (e.g., metallic titanium or titanium oxide).Conjointly, the lower region of the coater adjacent such target canoptionally be provided with an oxidizing atmosphere. With photocatalytictitanium oxide coatings and other high index photocatalysts inparticular, it is especially desirable not to subject such coatings tosubsequent overspraying, as overspray on such coatings will tend to bemore visible than overspray on other types of coatings, due to thesomewhat reflective nature of these coatings.

In certain advantageous embodiments, the optional upward coatingapparatus 55 comprises a lower sputtering target of the nature describedin U.S. patent application Ser. No. 60/262,878, the entire teachings ofwhich are incorporated herein by reference.

If a photocatalytic coating applied to the bottom major surface of asubstrate is subjected to overspray from a subsequent downward coatingoperation, the desired photocatalytic properties can be jeopardized.Thus, in embodiments wherein a photocatalytic coating is applied to thebottom major surface of a substrate by an upward coating operation, thisupward coating operation is desirably not followed by any subsequentdownward coating operation in the coater.

In embodiments of the invention wherein one apparatus (e.g., an ion gunor a coating apparatus) is at a location further along the path ofsubstrate travel than another apparatus (e.g., an ion gun or a coatingapparatus), these apparatuses are of course not vertically aligneddirectly above/below each another. Preferably, though not necessarily,they are in separate deposition zones (which may be isolated from eachother by gas separation and/or a curtain, wall, or other divider), andin some cases they are in separate chambers of the coater. The term“titanium-containing” material refers to any material that includes atleast some titanium (the same convention is used for other materials).When the ion gun 50 is used to clean the bottom surface of thesubstrate, argon or another inert gas is preferably used for thecleaning (i.e., Ar gas is used in the ion gun to accelerate Ar+ ionstoward the substrate's bottom surface). In some cases, the ion gun whenused to clean the bottom surface of the substrate is operated to producean ion beam having an ion energy of between about 300 eV and about 5,000eV, perhaps more preferably between about 1,500 eV and about 2,000 eV,and perhaps optimally between about 1,400 eV and about 1,600 eV.Preferably, the ion gun is operated to produce an ion bean that impingesthe substrate's bottom surface at an angle of about 90 degrees, orelsewhere within a range of between about 30 and about 90 degrees. Incertain embodiments, the substrate is fully processed (e.g., both of itsmajor surfaces can be coated) in a single pass through the coater 5.

While there have been described what are believed to be preferredembodiments of the present invention, those skilled in the art willrecognize that other and further changes and modifications can be madewithout departing from the spirit of the invention, and all such changesand modifications should be understood to fall within the scope of theinvention.

1. A method of processing a sheet-like glass substrate, the sheet-likeglass substrate having a top major surface and an opposite, bottom majorsurface, the method comprising: a) providing a coater adapted forapplying coating onto the substrate, the coater comprising a substratesupport defining a path of substrate travel extending through thecoater, a downward coating apparatus positioned above the path ofsubstrate travel, and an ion gun positioned beneath the path ofsubstrate travel, wherein the ion gun is at a location further along thepath of substrate travel than the downward coating apparatus; b)conveying the substrate along the path of substrate travel; c) operatingthe downward coating apparatus to coat the top major surface of thesubstrate; and d) operating the ion gun to emit an ion beam toward thebottom major surface of the substrate, said operation of the ion gunbeing performed to treat the bottom major surface of the substrate asthe substrate travels the path of substrate travel so that the entirebottom major surface of the substrate will have been treated once travelof the substrate past the ion gun is complete to remove any oversprayedcoating that was inadvertently deposited upon marginal portions of thebottom major surface of the substrate during said operation of thedownward coating apparatus.
 2. The method of claim 1 wherein thesubstrate is maintained in a horizontal orientation during saidconveyance of the substrate along the path of substrate travel.
 3. Themethod of claim 1 wherein the substrate is a sheet of glass that is onthe substrate support during said conveyance, and wherein other sheetsof glass are also on the substrate support, such sheets of glass beingspaced-apart from one another on the substrate support and conveyed insuch a spaced-apart configuration.
 4. The method of claim 1 wherein thesubstrate support comprises a plurality of spaced-apart transportrollers, the method comprising rotating at least one of the transportrollers to achieve said conveyance of the substrate along the path ofsubstrate travel.
 5. The method of claim 4 wherein said operation of theion gun emits said ion beam upwardly between an adjacent pair of thespaced-apart transport rollers.
 6. The method of claim 1 wherein thedownward coating apparatus is a downward sputtering apparatus comprisingan upper sputtering target positioned above the path of substratetravel, and wherein said operation of the downward coating apparatuscomprises establishing a plasma adjacent said upper sputtering target.7. The method of claim 1 wherein the downward coating apparatus is achemical vapor deposition apparatus, and wherein said operation of thedownward coating apparatus comprises delivering precursor gas to anupper region of the coater.
 8. The method of claim 1 wherein thedownward coating apparatus comprises an upper ion gun, the upper ion gunbeing adapted for ion beam coating deposition, and wherein saidoperation of the downward coating apparatus comprises operating theupper ion gun to emit an ion beam toward the top major surface of thesubstrate.
 9. The method of claim 1 further comprising an upward coatingapparatus, the upward coating apparatus being positioned beneath thepath of substrate travel at a location further along the path ofsubstrate travel than the ion gun, the method comprising operating theupward coating apparatus to coat the bottom major surface of thesubstrate after said operation of said ion gun has removed anyoversprayed coating from the bottom major surface of the substrate. 10.The method of claim 9 wherein said operation of the upward coatingapparatus is performed after all other coating of the substrate in thecoater has been performed.
 11. The method of claim 9 wherein thesubstrate is not conveyed beneath any operating downward coatingapparatus in the coater after said operation of the upward coatingapparatus, such that marginal portions of coating applied to the bottommajor surface of the substrate will not be concealed by oversprayedcoating from any subsequent downward coating apparatus in the coater.12. The method of claim 9 wherein said operation of the upward coatingapparatus is performed in a final chamber of the coater.
 13. The methodof claim 9 wherein the bottom major surface of the substrate is coatedwith a coating having a total optical thickness of less than about 690Å.14. The method of claim 13 wherein the top major surface of thesubstrate is coated with a coating having a total optical thickness ofat least about 1,000Å.
 15. The method of claim 9 wherein said operationof the upward coating apparatus comprises depositing on the bottom majorsurface of the substrate a surface-effect coating selected from thegroup consisting of a photocatalytic coating, a hydrophilic coating, anda hydrophobic coating.
 16. The method of claim 15 wherein thesurface-effect coating comprises titanium oxide and/or silicon oxide.17. The method of claim 16 wherein the surface-effect coating is aphotocatalytic coating comprising titanium oxide.
 18. The method ofclaim 9 wherein the upward coating apparatus is an upward sputteringapparatus comprising a lower sputtering target positioned beneath thepath of substrate travel, and wherein said operation of the upwardcoating apparatus comprises establishing a plasma adjacent said lowersputtering target.
 19. The method of claim 9 wherein the upward coatingapparatus is an evaporation coating apparatus, and wherein saidoperation of the upward coating apparatus comprises positioning a sourceof coating material to be evaporated in a lower region of the coater.20. The method of claim 9 wherein the upward coating apparatus is achemical vapor deposition apparatus, and wherein said operation of theupward coating apparatus comprises delivering precursor gas to a lowerregion of the coater.
 21. The method of claim 9 wherein the upwardcoating apparatus comprises a further ion gun, said further ion gunbeing adapted for ion beam coating deposition, and wherein saidoperation of the upward coating apparatus comprises operating saidfurther ion gun to emit an ion beam toward the bottom major surface ofthe substrate.
 22. The method of claim 1 wherein the operating the iongun to emit an ion beam towards a bottom major surface of the substratecomprises emitting ions from said ion gun that span substantially theentire width of said bottom major surface.
 23. The method of claim 1wherein the ion gun is part of a plurality of ion guns, and theoperating the ion gun to emit an ion beam towards a bottom major surfaceof the substrate comprises emitting ions from said plurality of ion gunsthat span substantially the entire width of said bottom major surface.24. A method of processing a sheet-like glass substrate, the sheet-likeglass substrate having a top major surface and an opposite, bottom majorsurface, the method comprising: a) providing a coater adapted forapplying coating onto the substrate, the coater comprising a substratesupport defining a path of substrate travel extending through thecoater, wherein an ion gun is positioned beneath the path of substratetravel, and wherein an upward coating apparatus is positioned beneaththe path of substrate travel at a location further along the path ofsubstrate travel than the ion gun; b) conveying the substrate along thepath of substrate travel; c) operating the ion gun to emit an ion beamtoward the bottom major surface of the substrate, the ion beamcomprising accelerated ions that strike the bottom major surface of thesubstrate as the substrate travels the path of substrate travel so thatthe entire bottom major surface of the substrate will have been treatedonce travel of the substrate past the ion gun is complete; and d)operating the upward coating apparatus to deposit a photocatalyticcoating on the bottom major surface of the substrate.
 25. The method ofclaim 24 wherein the upward coating apparatus is an upward sputteringapparatus comprising a lower sputtering target positioned beneath thepath of substrate travel, the lower target being sputtered to depositthe photocatalytic coating on the bottom major surface of the substrate.26. The method of claim 25 wherein the lower target comprises atitanium-containing target material, the lower target being sputtered inan oxidizing atmosphere.
 27. The method of claim 24 wherein thephotocatalytic coating is deposited so as to have a total opticalthickness of less than about 690Å.
 28. The method of claim 24 whereinsaid operation of the upward coating apparatus to apply thephotocatalytic coating is performed after all other coating of thesubstrate in the coater has been performed.
 29. The method of claim 24wherein the substrate is not conveyed beneath any operating downwardcoating apparatus in the coater after said operation of the upwardcoating apparatus, such that marginal portions of coating applied to thebottom major surface of the substrate will not be concealed byoversprayed coating from any subsequent downward coating apparatus inthe coater.
 30. The method of claim 24 wherein said operation of theupward coating apparatus is performed in a final chamber of the coater.31. The method of claim 24 wherein the ion gun is at a location furtheralong the path of substrate travel than a downward coating apparatus,the method comprising operating the downward coating apparatus to coat atop major surface of the substrate, said operation of the ion gun beingperformed to remove from the bottom major surface of the substrateoversprayed coating inadvertently deposited upon marginal portions ofthe bottom major surface of the substrate during said operation of thedownward coating apparatus.
 32. The method of claim 24 wherein the ionbeam comprises accelerated ions that span substantially the entire widthof said bottom major surface of the substrate.
 33. A method ofprocessing a sheet-like substrate, the method comprising: a) providing acoater adapted for applying coating onto the substrate, the coatercomprising a substrate support defining a path of substrate travelextending through the coater, a downward coating apparatus positionedabove the path of substrate travel, an ion gun positioned beneath thepath of substrate travel, wherein the ion gun is at a location furtheralong the path of substrate travel than the downward coating apparatus,and an upward coating apparatus positioned beneath the path of substratetravel at a location farther along the path of substrate travel than theion gun, the method comprising: b) conveying the substrate along thepath of substrate travel; c) operating the downward coating apparatus tocoat a top major surface of the substrate; d) operating the ion gun toemit an ion beam toward a bottom major surface of the substrate, saidoperation of the ion gun being performed to remove from the bottom majorsurface of the substrate any oversprayed coating that was inadvertentlydeposited upon marginal portions of the bottom major surface of thesubstrate during said operation of the downward coating apparatus; ande) operating the upward coating apparatus to coat the bottom majorsurface of the substrate after said operation of said ion gun hasremoved any oversprayed coating from the bottom major surface of thesubstrate, wherein said operation of the upward coating apparatus isperformed after all other coating of the substrate in the coater hasbeen performed.
 34. The method of claim 33 wherein the operating the iongun to emit an ion beam toward a bottom major surface of the substratecomprises emitting ions from said ion gun that span substantially theentire width of said bottom major surface.
 35. The method of claim 33wherein the substrate is maintained in a horizontal orientation duringsaid conveyance of the substrate along the path of substrate travel. 36.The method of claim 33 wherein the substrate support comprises aplurality of spaced-apart transport rollers, the method comprisingrotating at least one of the transport rollers to achieve saidconveyance of the substrate along the path of substrate travel.
 37. Themethod of claim 36 wherein said operation of the ion gun emits said ionbeam upwardly between an adjacent pair of the spaced-apart transportrollers.
 38. The method of claim 33 wherein the downward coatingapparatus is a downward sputtering apparatus comprising an uppersputtering target positioned above the path of substrate travel, andwherein said operation of the downward coating apparatus comprisesestablishing a plasma adjacent said upper sputtering target.
 39. Themethod of claim 33 wherein said operation of the upward coatingapparatus is performed in a final chamber of the coater.
 40. The methodof claim 33 wherein said operation of the upward coating apparatuscomprises depositing on the bottom major surface of the substrate asurface-effect coating selected from the group consisting of aphotocatalytic coating, a hydrophilic coating, and a hydrophobiccoating.
 41. The method of claim 33 wherein the upward coating apparatusis an upward sputtering apparatus comprising a lower sputtering targetpositioned beneath the path of substrate travel, and wherein saidoperation of the upward coating apparatus comprises establishing aplasma adjacent said lower sputtering target.
 42. A method of processinga sheet-like substrate, the method comprising: a) providing a coateradapted for applying coating onto the substrate, the coater comprising asubstrate support defining a path of substrate travel extending throughthe coater, wherein an ion gun is positioned beneath the path ofsubstrate travel, and wherein an upward coating apparatus is positionedbeneath the path of substrate travel at a location further along thepath of substrate travel than the ion gun; b) conveying the substratealong the path of substrate travel; c) operating the ion gun to emit anion beam toward a bottom major surface of the substrate, the ion beamcomprising accelerated ions that strike the bottom major surface of thesubstrate; and d) operating the upward coating apparatus to deposit aphotocatalytic coating on the bottom major surface of the substrate,wherein said operation of the upward coating apparatus to apply thephotocatalytic coating is performed after all other coating of thesubstrate in the coater has been performed.
 43. The method of claim 42wherein the substrate is maintained in a horizontal orientation duringsaid conveyance of the substrate along the path of substrate travel. 44.The method of claim 42 wherein the substrate support comprises aplurality of spaced-apart transport rollers, the method comprisingrotating at least one of the transport rollers to achieve saidconveyance of the substrate along the path of substrate travel.
 45. Themethod of claim 44 wherein said operation of the ion gun emits said ionbeam upwardly between an adjacent pair of the spaced-apart transportrollers.
 46. The method of claim 42 wherein the downward coatingapparatus is a downward sputtering apparatus comprising an uppersputtering target positioned above the path of substrate travel, andwherein said operation of the downward coating apparatus comprisesestablishing a plasma adjacent said upper sputtering target.
 47. Themethod of claim 42 wherein the upward coating apparatus is an upwardsputtering apparatus comprising a lower sputtering target positionedbeneath the path of substrate travel, the lower target being sputteredto deposit the photocatalytic coating on the bottom major surface of thesubstrate.
 48. The method of claim 47 wherein the lower target comprisesa titanium-containing target material, the lower target being sputteredin an oxidizing atmosphere.
 49. The method of claim 42 wherein saidoperation of the upward coating apparatus is performed in a finalchamber of the coater.
 50. The method of claim 42 wherein the operatingthe ion gun to emit an ion beam toward a bottom major surface of thesubstrate comprises emitting ions from said ion gun that spansubstantially the entire width of said bottom major surface.